| 尿塔物理断裂失效分析 |
| |
| 引用本文： | 丁春燕,杨 杰. 尿塔物理断裂失效分析[J]. 河北工业科技, 2008, 25(1): 21-23 |
| |
| 作者姓名： | 丁春燕 杨 杰 |
| |
| 作者单位： | 河北化工医药职业技术学院,河北石家庄,050026;河北科技大学老干部处,河北石家庄,050018 |
| |
| 摘 要： | 从能量角度对尿塔断裂进行分析,排除塔内化学爆炸,确定为尿塔物理断裂,并有针对性地进行失效分析。
|
| 关 键 词： | 多层包扎式筒体 环焊缝 焊接缺陷 失效分析 |
| 文章编号： | 1008-1534（2008）01-0021-03 |
| 收稿时间： | 2007-07-23 |
| 修稿时间： | 2007-10-10 |
Failure analysis of ureasynthetic tower's physical broken |
| |
| DING Chun-yan and YANG Jie. Failure analysis of ureasynthetic tower's physical broken[J]. Hebei Journal of Industrial Science & Technology, 2008, 25(1): 21-23 |
| |
| Authors: | DING Chun-yan and YANG Jie |
| |
| Affiliation: | 1.Hebei Chemical and Pharmaceutial College;Shijiazhuang Hebei 050026;China;2.Department of the Venerable;Hebei University of Science and Technology;Shijiazhuang Hebei 050018;China |
| |
| Abstract: | In view of energy analysis, chemical explosion inside the tower can be excluded, while physical broken is proved, and based on this, failure analysis can be made. |
| |
| Keywords: | muhilayer werping cylinder ring weld weld defects failure analysis |