利用旋涂法和喷墨印刷法在室温下沉积银导电层 |
| |
引用本文: | Author Josue J P Valeton,Ko Hermans,Cees W M Bastiaansen,Dirk J Broer,Jolke Perelaer,Ulrich S Schubert,Gregory P Crawford,Patrick J Smith,王晓芳[编译].利用旋涂法和喷墨印刷法在室温下沉积银导电层[J].中国印刷物资商情,2011(2):63-66. |
| |
作者姓名: | Author Josue J P Valeton Ko Hermans Cees W M Bastiaansen Dirk J Broer Jolke Perelaer Ulrich S Schubert Gregory P Crawford Patrick J Smith 王晓芳[编译] |
| |
作者单位: | [1]Laboratory for Simulation, Albert-Ludwigs-University Freiburg, Georges-Kohler Allee 102, 79110 Freiburg, Germany. [2]Department of Chemical Engineering, Eindhoven University of Technology, P O Box 513, NL-5600 MB Eindhoven, TheNetherlands. [3]NeoDec BV, Raiffeisenstraat 9, NL-5611 CH Eindhoven, The Netherlands. [4]Laboratory of Organic and Macromolecular Chemistry, Friedrich-Schiller-University Jena, Humboldtstr. 10, 07743 Jena,Germany. [5]College of Science, University of Notre Dame, Notre Dame, Indiana, 46656, USA. [6]不详, University of Notre Dame, Notre Dame, Indiana, 46656, USA. |
| |
摘 要: | 以具有低玻璃化温度的聚合物,如PET为基材,采用喷墨印刷法及旋涂法沉积含银金属有机油墨,经UV光固化及对苯二酚溶液处理生成银导电层,此过程在室温下进行,用时不到1min。结果表明银导电层的电导率是纯银的10%。本文也测试了沉积银导电层后PET膜的机械稳定性,发现电阻随着应变的增加呈线性增长,经过12000次变形试验后其电阻不再发生明显变化。
|
关 键 词: | 喷墨印刷 导电 沉积 银 利用 PET膜 对苯二酚 聚合物 |
Room Temperature Preparation of Conductive Silver Features Using Spin-Coating and Inkjet Printing |
| |
Institution: | Author Josue J P Valeton,Ko Hermans,Cees W M Bastiaansen,Dirk J Broer,Jolke Perelaer,Ulrich S Schubert, Gregory P Crawford ,Patrick J Smith 1 Laboratory for Simulation,Albert-Ludwigs-University Freiburg,Georges-Kohler Allee 102,79110 Freiburg,Germany. 2 Department of Chemical Engineering,Eindhoven University of Technology,P O Box 513,NL-5600 MB Eindhoven,The Netherlands. 3 NeoDec BV,Raiffeisenstraat 9,NL-5611 CH Eindhoven,The Netherlands. 4 Laboratory of Organic and Macromolecular Chemistry,Friedrich-Schiller-University Jena,Humboldtstr.10,07743 Jena, Germany. 5 College of Science,University of Notre Dame,Notre Dame,Indiana,46656,USA. |
| |
Abstract: | Inkjet printing and spin-coating have been used to prepare patterns using a silver-containing metalloorganic decomposition ink.The patterned ink was reduced to silver by exposure to UV light and subsequent treatment with hydroquinone solution.This process,which took less than a minute,was performed at room temperature,which allowed low glass transition temperature polymeric substrates,such as PET,to be used.The conductivity of the silver patterns was found to be 10% that of bulk silver.The mechanical stability was also measured,with a linear increase in resistance seen for increasing strain, and no significant change in resistance seen after 12000 cyclic deformations. |
| |