| 镍-磷-碳化硅镀层制备工艺的研究 |
| |
| 引用本文： | 宿辉.镍-磷-碳化硅镀层制备工艺的研究[J].价值工程,2014(6):294-295. |
| |
| 作者姓名： | 宿辉 |
| |
| 作者单位： | 黑龙江工程学院材料与化学工程学院,哈尔滨150050 |
| |
| 基金项目： | 黑龙江省教育厅项目（11551390）. |
| |
| 摘 要： | 为了提高化学复合镀层的性能,采用纳米碳化硅颗粒为增强体制备了镍-磷-碳化硅化学复合镀层,研究了温度、pH、搅拌速率对镍-磷-碳化硅镀层沉积速率的影响,确定了最佳施镀工艺:温度为84℃、pH值为4.6、搅拌速度为200r·min-1。
|
| 关 键 词： | 碳化硅颗粒 化学复合镀层 工艺参数 纳米 |
Study on Technology of Nickel-Phosphorus-Silicon Carbide Particle Coating |
| |
| Institution: | XU Hui ( College of Materials and Chemical, Engineering Heilongjiang Institute of Technology, Harbin 150050, China ) |
| |
| Abstract: | In order to improve the properties of electroless composite coating, the Nickel- Phosphorus-Silicon carbide particle coating electroless composite coating added Silicon carbide particle was prepared and various parameters on the Nickel- Phosphorus-Silicon carbide particle coating were studied systematically. The experimental results show that： temperature, pH stirring speed deposition rate had a greater influence. It was coufirmd that the temperature was 84℃, the pH was 4.6, the best stirring rate was 200r/mira^-1. |
| |
| Keywords: | Silicon carbide particle electroless composite coating technological parameter Nanometer |