包铝铁红产品耐高温性能的研究

随着建筑材料行业的迅速发展和瓷质玻化砖的广泛应用,市场上对具有耐高温性质的铁红颜料需求很大,但是目前国产氧化铁红煅烧到800℃以上时会发生烧结和还原,严重影响了产品质量。通过比较原料铁红、包铝铁红和超声波分散后的包铝铁红3种产品之间的耐高温性能,得出结论：经过超声波搅拌分散15min后的包铝铁红产品,最高耐温可达1200℃,而且无烧结情况发生。通过观察铁红颗粒包覆Al2O3前后的TEM图片,发现Al2O3可以在铁红颗粒外面形成一层包膜,使粒子之间被包膜隔开,因此产品的耐烧温度被提高,而且不会烧结在一起。     

Measurement of greenhouse gas emissions from agriculture: economic implications for policy and agricultural producers*

If agriculture were to be included in Australia’s carbon price scheme, a key decision for government would be how to estimate greenhouse gas emissions. We explore the consequences of three different methods for measuring on‐farm emissions: national accounting methods, an amended version of those methods and use of best‐available local data. Estimated emissions under the three methods can vary widely; for example, on a case study farm in Western Australia, local data indicated 44 per cent lower emissions than did the national accounts method. If on‐farm emissions are subject to an emissions price, the impact on farm profit is large and varies considerably with different measurement methods. For instance, if a price of $23/t of CO2‐e applies then farm profit falls by 14.4–30.8 per cent depending on the measurement method. Thus, the choice of measurement method can have large distributional consequences. On the other hand, inaccurate measurement results in relatively minor deadweight losses. On‐farm sequestration through reafforestation may lessen the impact of an emissions price on farm businesses, although it will require a high carbon price to be viable, especially if sequestration rates are underestimated or low.     

国内氧化铁行业现状及发展趋势

本文介绍了我国氧化铁行业现状、存在问题和发展趋势，并对氧化铁今后的发展提出了建议。     

低分子量PEO均聚物薄膜的结晶研究

采用DSC测试了聚氧化乙烯（PEO）均聚物的结晶温度（TC）和熔融温度（Tm）,利用偏光显微镜（POM）研究了PEO的结晶温度、结晶时间以及PEO的相对分子质量等因素对PEO结晶形态的影响.结果表明：结晶温度对PEO均聚物结晶形态的影响比较显著,在较低温度下（室温下）,PEO形成普通球晶,并随结晶温度升高球晶尺寸逐渐增大,当结晶温度在室温以上时,PEO结晶形态比较完善,结晶尺寸比较大,而且PEO的结晶除黑十字消光外,还带有环形裂纹;结晶时间和PEO相对分子质量的改变只能够影响PEO晶体的尺寸,对PEO晶体的形态并没有太大的影响.     

Envirox™ fuel-borne catalyst: Developing and launching a nano-fuel additive

The paper presents a product case study tracing the challenges of commercialization from research and product development to market launch. Envirox™ is a diesel fuel additive containing nanoparticles of cerium oxide, which enables fuel efficiency gains alongside reductions in harmful emissions such as black carbon (soot). The case traces developmental stages from lab experimentation and performance data sets, to raising finance, securing manufacturing capability and market testing in Hong Kong and the UK. The paper raises a number of generic and specific issues facing innovative small, university spin-out companies engaged in introducing nano-products to the market-place.     

复合氧化物载体用于加氢脱硫催化剂的研究进展

载体是加氢脱硫(HDS)研究的重要方面,在过去的20年来,复合载体受到了极大的关注.本文将集中综述Mo和W催化剂的复合氧化物载体.为了便于讨论,将它们分成含Al2O3的复合氧化物载体,含TiO2的复合氧化物载体,含ZrO2的复合氧化物载体和所有其它复合氧化物载体,进行分别论述.     

烟气脱硝技术及其在不锈钢酸洗废气治理中的应用

文章概述了国内外烟气脱硝常用技术的特点、原理,对目前应用较多的NOX治理技术催化还原法、液体吸收法和固体吸附法进行了分析比较,将催化还原法与氧化吸收法联合应用于不锈钢酸洗废气治理中,工程实践表明,酸洗废气可达标排放。     

X射线荧光光谱法测定高岭土中氧化镁含量

将样品粉碎至300目后压片制样,直接用X射线荧光光谱仪测定,外标法定量。试验数据表明,在0-1.0%范围内,线性良好,RMS为0.02296%,品质系数K为0.036970.1%;平均回收率在90%-110%之间,相对标准偏差为0.915%。本法简化了样品前处理过程,缩短了分析时间,检测周期减少到20m in左右。     

氧化锌的制备及表征

采用直接沉淀法和均匀沉淀法制备氧化锌,考察了反应物配比、反应温度、反应时间对产率的影响,同时考察了煅烧温度、煅烧时间对产品外观的影响,通过测定堆积密度、红外光谱对产品进行了表征,从而确定了最佳的制备工艺条件。研究结果表明,最佳的制备方法为直接沉淀法,最佳的制备工艺条件:碳酸铵与氯化锌的物质的量比为1.2∶1,反应温度为60℃,反应时间为2.0 h,煅烧温度为450℃,煅烧时间为1.5 h。     

进口含镉氧化锌富集物的表征和鉴别探讨

采用X射线荧光光谱仪(XRF)、X射线衍射光谱仪(XRD)及标准方法等分析技术手段,对送检的某进口含镉氧化锌富集物样品进行表征。将样品的外观、组成和理化特征,与委托方提供货物来源、含锌矿物、含氧化锌产品及相关文献等进行比对和匹配。结果表明:样品外观呈阙绿色粉末状,部分结块,未见明显夹杂物;样品含Zn、Pb、S、Fe、Si、Cl、Cd等元素,主物相ZnO含量为49.7%,含少量Zn5(OH)8Cl2.H2O、Pb(OH)Cl、K(AlSi2O6)和ZnS等相;样品中杂质及有害元素Fe、As、Cd、F、Cl和Hg含量分别为3.55%、0.28%、0.78%、0.32%、4.25%和<0.002%。样品来源、外观质量符合YS/T 1343-2019《锌冶炼用氧化锌富集物》要求,但样品化学成分中的ZnO含量和杂质Cd含量不满足标准要求。依照《中华人民共和国固体废物污染环境防治法》和GB 34330-2017《固体废物鉴别标准通则》判定该含镉氧化锌富集物为固体废物。